Mypoxy HSHB AL Mastic 1000

Products->Protective Coatings->Epoxy

Mypoxy HSHB AL Mastic 1000

 

Product

Two component Surface Tolerant (Polyamine cured) coating pigmented with aluminium to provide better barrier protection. It's a high solids, abrasion resistant coating, which can be applied directly to mechanically prepared shop primer or suitably prepared bare steel.

Recommended Use

HSHB AL Mastic 1000 is recommended as primer, intermediate coat or as topcoat provides long lasting protection in environments with high corrosivity. It can be used as single coat system in atmospheric and immersed environments. Recommended for Steel Structures, Mining Equipments, Pipelines, Storage Tanks etc including hand prepared rusty steel, hydroblasted steel, and a wide range of intact, aged coatings in Infrastructure projects, Bridges, Refinaries Pipelines, Chemical Plants, Steel Plants, Cement Plants, Petrochemicals Plants etc.

Specification & Other Information
Colour

: Aluminium

Finish

: Semi Glossy

Soiled by Volume

: 84 ± 2%

Supply Weight (Kg/Ltr)

: 1.40±0.05

Flash Point

: 33° C

Dry Heat Resistance

: Intermittent : 120°C, Continuous: 120°C
Shelf Life : 12 months
Dry Film Thickness

: 150-250µ in single coat
Wet Film Thickness

: 175-300µ in single coat
Theoretical Coverage Rate : 5.5 sq.mt / lit at recommended DFT of 150µ

Surface Preparation

All surfaces to be coated should be clean, absolutely dry and oil or moisture free before painting application. Oil and grease should be removed by solvent cleaning.

Repair Cases: Corroded areas should be power tool cleaned to St3 or blast cleaned to Sa2 or better. Existing system should be dry and free from loose paint, salt, grease and other contaminants prior to over coating.

New steel: Abrasive blasting to Sa 2½ (ISO 8501-1:2007). HSHB AL 1000 is designed to apply directly over properly solvent cleaned steel as well. However all damage of primer and contamination from storage and fabrication should be thoroughly cleaned prior to final painting.

Maintenance: Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly by power tool cleaning to St 3 (ISO 8501-1:2007) (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½ (ISO 8501-1:2007). Improved surface preparation will improve the performance of the product.

Aged Surface: Mypoxy HSHB AL 1000 is suitable for over coating a limited range of intact, tightly adherent aged coatings. Loose or flaking coatings should be removed back to a firm edge. Glossy finishes require light abrasion by emery paper or power tool to provide a physical key.

Application Data
Application Method

: Airless Spray, Brush/ Roller (Only Touch up)

Mixing Ratio

: 3 Part (Base) : 1 Part (Hardener)

Pot Life

: One Hours at 30°C

Thinner and Cleaner 

: Mypoxy Epoxy Thinner 

Airless Nozzle Orifice

: 0.53 - 0.78mm

Nozzle Pressure

: 211 kg/cm² or 3000 psi

Working Precautions: Material should not be allowed to remain in pipeline, hoses, gun or spray equipment. Thoroughly flush all equipment with Epoxy thinner. Once units of paint have been mixed they should not be resealed and it is advised that after prolonged stoppages, the work should recommences with freshly mixed units.

Maintenance: Clean all equipment immediately after use with Epoxy thinner. It is good working practice to periodically flush out spray equipment during the course of the working day. All surplus materials and empty containers should be disposed of in accordance with appropriate regional regulations/legislation.

Drying Characteristics
Surface Dry

: 60 mins

Touch Dry (to handle)

: 3 Hours

Hard Dry

: 16 Hours

Overcoating Interval

: Minimum 6 Hours & Maximum 15Days
Drying and curing times are determined at 30°C under controlled temperatures and relative humidity below 85%, and at average of the DFT range for the product.

Compatibility
Previous Coating

: Epoxy, Inorganic Zinc Silicates

Subsequent Coating

: Epoxy, Polyurethanes, Alkyds, Modified Alkyds, Acrylics

Storage

This is solvent based coating and the containers should be kept in a dry, cool, well ventilated space and away from sources of heat and ignition. Containers must be kept tightly closed.

Caution

This product is for professional use only. The paint applicators should be trained, experienced and have the capability and equipment to mix and apply the coatings correctly as instructed. Applicators should use appropriate protection equipment when using this product.

This is solvent based product and should be use under well ventilated conditions. Do not inhale spray mist. Skin contact should be avoided. In case of spillage on the skin, it should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water.

Limitation of Liability
This information is given to the best of our knowledge. Because of the multitude of formulations, production, and application conditions, all the above-mentioned statements have to be adjusted to the circumstances of the processor. Our products are often used under conditions beyond MSPL's control. MSPL cannot guarantee anything but the quality of the product itself. No liabilities can be derived from this fact for individual cases. This issue replaces all previous versions – Printed in India.